Technical Datasheet | Supplied by CP-Polymer-Technik
WELLAMID 6600/508 HWUVCP is an unreinforced heat and heat ageing stabilized PA (polyamide) 66 grade. Exhibits improved impact strength and functional UV-stabilization. It can be processed using injection molding. Suitable for E&E (Electrical & Electronics) and automotive industry. Potential applications include mechanical, medical, food, and toys industry. Approved by many German and European car manufacturers. Listed on C-UL, LNE- and VDE certificates.
Product Type
PA (Polyamide, Nylon) > PA 66 (Nylon 66)
Product Status
Applications/ Recommended for
  • Automotive
  • Electrical markets
  • Electronics / Computers
  • Healthcare / Medical
  • Households products/ Consumer Goods > Toys
  • Injection molding - thermoplastics

WELLAMID 6600/508 HWUVCP Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Tensile Strength
75 MPa
(at Yield, 50 mm/min, Dry (Freshly molded))
ISO 527
Tensile Strength
50 MPa
(at Yield, 50 mm/min, Moist (After Conditioning))
ISO 527
Tensile Strain
5 %
(at Yield, 23°C, 50 mm/min, Dry (Freshly molded))
ISO 527

WELLAMID 6600/508 HWUVCP Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Drying Temperature
75 °C
Drying Time
2 - 4 hr
Processing (Melt) Temp
260 - 290 °C
Help us improve the Universal Selector

You can’t find what you are looking for? Please report missing products / suppliers, point out errors, or simply tell us how we could make the Universal Selector better.

Access Reliable
Product Information

Database of 145235 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top