Durethan® BCF 30 X H2.0 901510

Technical Datasheet | Supplied by Lanxess
DURETHAN®BCF 30 X H 2.0 901510 is a heat aging stabilized polyamide (PA 6) grade reinforced with 30% glass fiber and carbon fiber. Possesses high mechanical strength, good electrical insulation properties and high stiffness. Exhibits good toughness, low friction, dynamic load bearing properties and good processability. Provides high wear-, abrasion-, shock 80 to 160 °C long-term) and chemicals such as fuels, lubricants, solvents and cleaning agents. Is suitable for processing by injection molding. Recommended for automotive, electrical/electronics industries and buildings and construction sector. Complies with REACH (Regulation EC No. 1907/2006) and RoHS.
download
Product Type
PA (Polyamide, Nylon) > PA 6 (Nylon 6)
Physical Form
Granules
Appearance
Black

Durethan® BCF 30 X H2.0 901510 Properties

Thermal Properties

Value & Unit
Test Condition
Test Method
Melting Point
220 °C
(10°C/min)
ISO 11357-3
Vicat Softening Temperature
214 °C
(50 N; 120 °C/h)
ISO 306
Ignition Temperature
> 400 °C
( )

Durethan® BCF 30 X H2.0 901510 Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Processing (Melt) Temp
270 - 290 °C
Permitted Residence Time
4 - 10 minutes
Mold Temperature
80 - 120 °C
Help us improve the Universal Selector

You can’t find what you are looking for? Please report missing products / suppliers, point out errors, or simply tell us how we could make the Universal Selector better.

Access Reliable
Product Information

Database of 93166 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top