Technical Datasheet | Supplied by SABIC
LNP™ LUBRICOMP™ Compound UX05051 by SABIC is based on polyphthalamide (PPA) resin containing glass fiber and PTFE. This heat stabilized, flame retardant & hot water moldable grade offers wear resistance and high heat resistance. It displays mold release properties. It is processed by injection molding.
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
LNP™ LUBRICOMP™ Compound UX05051
Technical Datasheet | Supplied by SABIC
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
Product Type
PA (Polyamide, Nylon) > PPA
Product Status
COMMERCIAL
Geographical Availability
Africa, Asia / Pacific, Central and Eastern Europe, Middle East and Central Asia, North America, South and Central America, Western Europe
Applications/ Recommended for
Injection molding - thermoplastics
Key Features
  • Filled, Glass Fiber
  • Filled, PTFE
  • Flame retarded
  • Heat Resistance, High
  • Heat stabilized
  • Mold Release, Good
  • Moldability, Hot Water
  • Wear resistance, Good

LNP™ LUBRICOMP™ Compound UX05051 Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Flexural Yield Strength
188 MPa
(At 2 mm/min) 
ISO 178
Flexural Modulus
10700 MPa
(At 2 mm/min) 
ISO 178
Tensile Strength at Break
138 MPa
(At 5 mm/min) 
ISO 527

LNP™ LUBRICOMP™ Compound UX05051 Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Drying Temperature
80 °C
Drying Time
4 hr
Melt Temperature
305 - 315 °C
Want to list or
update your products?
Want to report errors or
suggest improvements?
Access Reliable
Product Information

Database of 99992 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top