LNP™ LUBRICOMP™ Compound UX06427

Technical Datasheet | Supplied by SABIC
LNP™ LUBRICOMP™ Compound UX06427 by SABIC is based on polyphthalamide (PPA) resin containing 30% carbon fiber and 15% PTFE. This heat stabilized & hot water moldable grade offers wear resistance, high heat resistance and electrical conductivity. It displays mold release properties. It is processed by injection molding.
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
LNP™ LUBRICOMP™ Compound UX06427
Technical Datasheet | Supplied by SABIC
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
Product Type
PA (Polyamide, Nylon) > PPA
Product Status
COMMERCIAL
Geographical Availability
Africa, Asia / Pacific, Central and Eastern Europe, Middle East and Central Asia, North America, South and Central America, Western Europe
Applications/ Recommended for
Injection molding - thermoplastics
Key Features
  • Electrically Conductive
  • Filled, Carbon fiber
  • Filled, PTFE
  • Heat Resistance, High
  • Heat stabilized
  • Mold Release, Good
  • Moldability, Hot Water
  • Wear resistance, Good

LNP™ LUBRICOMP™ Compound UX06427 Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Flexural Strength
311 MPa
(At Break, 1.3 mm/min, 50 mm span) 
ASTM D790
Flexural Modulus
19640 MPa
(At 2 mm/min) 
ISO 178
Tensile Strength at Break
227 MPa
(At 5 mm/min) 
ISO 527

LNP™ LUBRICOMP™ Compound UX06427 Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Drying Temperature
120 °C
Drying Time
4 hr
Moisture Content
< 0.06 %
Want to list or
update your products?
Want to report errors or
suggest improvements?
Access Reliable
Product Information

Database of 99992 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top