LNP™ THERMOCOMP™ Compound LX97024

Technical Datasheet | Supplied by SABIC
LNP™ THERMOCOMP™ Compound LX97024 by SABIC is based on polyetheretherketone (PEEK) resin containing 15% glass fiber and 5% PTFE. This internally lubricated grade displays high heat resistance, easy molding properties, high stiffness and wear resistance. It exhibits high modulus. This grade is processed by injection molding.
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
LNP™ THERMOCOMP™ Compound LX97024
Technical Datasheet | Supplied by SABIC
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
Product Type
PK (Polyketone) > PEEK
Product Status
COMMERCIAL
Geographical Availability
Africa, Asia / Pacific, Central and Eastern Europe, Middle East and Central Asia, North America, South and Central America, Western Europe
Applications/ Recommended for
Injection molding - thermoplastics
Key Features
  • Filled, Glass Fiber
  • Filled, PTFE
  • Heat Resistance, High
  • Lubricated
  • Modulus, High
  • Stiffness, High
  • Wear resistance, Good

LNP™ THERMOCOMP™ Compound LX97024 Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Flexural Yield Strength
177 MPa
(At 2 mm/min) 
ISO 178
Flexural Modulus
6000 MPa
(At 2 mm/min) 
ISO 178
Tensile Strength at Break
114 MPa
(At 5 mm/min) 
ISO 527

LNP™ THERMOCOMP™ Compound LX97024 Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Drying Temperature
120 - 150 °C
Drying Time
4 hr
Moisture Content
< 0.1 %
Want to list or
update your products?
Want to report errors or
suggest improvements?
Access Reliable
Product Information

Database of 99992 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top