NORYL™ WM330G by SABIC is a 30% glass reinforced blend of impact modified polyphenylene ether (PPE) and polystyrene (PS). Exhibits good fatigue performance, excellent long-term hydrolytic stability, very low moisture absorption, heat and hot water resistance. Offers higher burst pressure, fluctuating pressure and creep rupture performance. Suitable for processing by injection molding. Recommended for a variety of building & construction and water management applications such as pump housings, impellers, shower/faucet, membrane housings and valves. Complies with FC EU, FDA for food contact, NSF/ANSI 61, ACS, WRAS and KTW/W270 certifications for cold, warm and hot water applications. NORYL™ WM330G also complies with UL 94 HB flame rating.
Product Type
PPE (Polyphenylene Ether) > PPE Alloy
Product Launch Date
Nov 21, 2019
Product Status

NORYL™ WM330G Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Tensile Strength at Break
131 MPa
(At 5 mm/min)
ISO 527
Tensile Strain
2.4 %
(At Break, 5 mm/min)
ISO 527
Tensile Modulus
9475 MPa
(At 1 mm/min)
ISO 527

NORYL™ WM330G Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Drying Temperature
100 - 120 °C
Drying Time
2 - 4 hr
Moisture Content
< 0.02 %
Help us improve the Universal Selector

You can’t find what you are looking for? Please report missing products / suppliers, point out errors, or simply tell us how we could make the Universal Selector better.

Access Reliable
Product Information

Database of 145857 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top