| Property |
PC/PBT BLEND |
| Electrical |
| Dielectric Constant |
2.95-3.14 |
| Dissipation Factor x 10-4 |
190-300 |
| Volume Resistivity x 1015, Ohm.cm |
16-17 |
| Mechanical |
| Elongation at Break, % |
4-175 |
| Elongation at Yield, % |
4.4-4.5 |
| Flexural Modulus, Gpa |
1.6-3.9 |
| Toughness (Notched Izod Impact at Room Temperature), J/m |
50-960 |
| Toughness at Low Temperature (Notched Izod Impact at Low Temperature), J/m |
170-640 |
| Young's Modulus, GPa |
1.8-2.3 |
| Physical |
| Density, g/cm3 |
1.17-1.3 |
| Shrinkage, % |
0.6-1.1 |
| Water Absorption 24 hours, % |
0.03-0.5 |
| UV Light Resistance |
Fair |
| Gamma Radiation Resistance |
Good |
| Sterilization Resistance (Repeated) |
Poor |
| Service Temperature |
| HDT @0.46 Mpa (67 psi), °C |
91-118 |
| HDT @1.8 Mpa (264 psi), °C |
60-121 |
| Max Continuous Service Temperature, °C |
60-121 |
| Thermal |
| Flammability, UL94 |
HB |