Biograde® C 5508

Technical Datasheet | Supplied by FKuR
Biograde® C 5508 by FKuR is a biodegradable, thermally stabilized, water insoluble, plasticizer-free cellulose acetate obtained from sustainable forestry wood. Contains high amount of renewable raw materials and additives. It has >60% bio-based carbon content (BCC). Exhibits high stiffness, high tensile & impact strength, short cycle times and good surface finish. Biograde® C 5508 is designed for processing by injection molding and cast film extrusion. Suitable for use as a packaging material in food contact applications and the production of components with thin wall thicknesses and long flow paths. Possible applications could be electronics, appliance, consumer products such as toothbrushes, ball-point pens, cutlery and toys. Complies with CLP regulation (EC) No. 1272/2008, EN 71-3, food contact regulations EN 10/2011 and US FDA.
download
Product Type
Cellulosic Polymers > CA
Physical Form
Granules
Appearance
Yellow, Translucent

Biograde® C 5508 Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Modulus of Elasticity
2460 MPa
ISO 527
Tensile Strength
55 MPa
ISO 527
Tensile Strain
7 %
(at Tensile Strength) 
ISO 527

Biograde® C 5508 Processing Guidelines

Injection Molding Properties

Value & Unit
Test Condition
Test Method
Feeding Zone Temperature
60 °C
Cylinder Zone 1 Temperature
190 °C
Machine Nozzle Temperature
200 - 220 °C
Want to list or
update your products?
Want to report errors or
suggest improvements?
Access Reliable
Product Information

Database of 100014 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top