LNP™ LUBRICOMP™ Compound WFL369

LNP™ LUBRICOMP™ Compound WFL369 by SABIC is based on polybutylene terephthalate (PBT) resin containing 30% glass fiber and 15% PTFE. This flame retardant grade offers wear resistance. It is processed by injection molding.

LNP™ LUBRICOMP™ Compound WFL369 Properties

Mechanical Properties

Value & Unit

Test Condition

Test Method

Flexural Modulus

8900 MPa

(At 2 mm/min)

ISO 178

Flexural Strength

155 MPa

(At 2 mm/min)

ISO 178

Tensile Modulus

11000 MPa

(At 1 mm/min)

ISO 527

Injection Molding Properties

Value & Unit

Test Condition

Test Method

Drying Temperature

120 °C

Drying Time

4 hr

Moisture Content

< 0.05 %

Want to list or
update your products?

View the listing options

Want to report errors or
suggest improvements?

Send a Feedback

Products with the same brand name

View more (585)

LNP™ LUBRICOMP™ Compound WFL369

LNP™ LUBRICOMP™ Compound WFL369 Properties

Mechanical Properties

LNP™ LUBRICOMP™ Compound WFL369 Processing Guidelines

Injection Molding Properties