LNP™ THERMOCOMP™ AM 6C004XXAR1

Technical Datasheet | Supplied by SABIC
LNP™ THERMOCOMP™ AM 6C004XXAR1 by SABIC is polycarbonate/polybutylene terephthalate (PC/PBT) resin containing 20% carbon fiber suitable for large format additive manufacturing (LFAM) applications. It offers improved chemical resistance, low warpage and good surface finish. LNP™ THERMOCOMP™ AM 6C004XXAR1 is processed by extrusion.
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
LNP™ THERMOCOMP™ AM 6C004XXAR1
Technical Datasheet | Supplied by SABIC
REQUEST A SAMPLE ORIGINAL DATASHEET CONTACT SUPPLIER
Product Type
PC (Polycarbonate) > PC + PBT
Product Status
COMMERCIAL
Geographical Availability
Africa, Asia / Pacific, Central and Eastern Europe, Middle East and Central Asia, North America, South and Central America, Western Europe
Applications/ Recommended for
  • 3D Printing/Additive Manufacturing
  • Extrusion
Key Features
  • Chemical resistance, Good
  • Filled, Carbon fiber
  • Surface Finish, Good
  • Warpage, Low

LNP™ THERMOCOMP™ AM 6C004XXAR1 Properties

Mechanical Properties

Value & Unit
Test Condition
Test Method
Tensile Stiffness
10.6 GPa
(At 5 mm/min, XZ Orientation)
ASTM D638 Modified
Tensile Stiffness
2.3 GPa
(At 5 mm/min, ZX Orientation)
ASTM D638 Modified
Tensile Strength
106 MPa
(At 5 mm/min, XZ Orientation)
ASTM D638 Modified

LNP™ THERMOCOMP™ AM 6C004XXAR1 Processing Guidelines

Extrusion Properties

Value & Unit
Test Condition
Test Method
Extruder L/D Ratio
24
Drying Temperature
110 °C
Drying Time
4 hr
Want to list or
update your products?
Want to report errors or
suggest improvements?
Access Reliable
Product Information

Database of 94799 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top