LNP™ THERMOCOMP™ Compound ZFM3314

LNP™ THERMOCOMP™ Compound ZFM3314 by SABIC is a flame retardant, impact modified, non-brominated, non-chlorinated polyphenylene ether and polystyrene (PPE+PS) blend reinforced with 20% glass fiber. It provides heat stability, high stiffness and low warpage. It is suitable for processing by injection molding. LNP™ THERMOCOMP™ Compound ZFM3314 is used in outdoor, lawn & landscape, sport/leisure, personal accessory, electrical components & infrastructure, commercial & home appliance, electronics and consumer applications.

LNP™ THERMOCOMP™ Compound ZFM3314 Properties

Mechanical Properties

Value & Unit

Test Condition

Test Method

Flexural Yield Strength

145 MPa

(At 2 mm/min)

ISO 178

Flexural Modulus

5800 MPa

(At 2 mm/min)

ISO 178

Tensile Strength at Break

95 MPa

(At 5 mm/min)

ISO 527

Injection Molding Properties

Value & Unit

Test Condition

Test Method

Drying Temperature

80 °C

Drying Time

2 - 8 hr

Drying Time (Cumulative)

8 hr

Want to list or
update your products?

View the listing options

Want to report errors or
suggest improvements?

Send a Feedback

Products with the same brand name

View more (851)

LNP™ THERMOCOMP™ Compound ZFM3314

LNP™ THERMOCOMP™ Compound ZFM3314 Properties

Mechanical Properties

LNP™ THERMOCOMP™ Compound ZFM3314 Processing Guidelines

Injection Molding Properties