Ultrafuse® PA

Ultrafuse® PA by BASF 3D Printing Solutions is co-polyamide 6-66 grade of intermediate viscosity designed for fused filament fabrication (FFF). It is the translation of BASF´s Ultramid® to the 3D printing space. Offers good fatigue & wear resistance as well as good impact resistance at low temperatures. Exhibits high mechanical strength, low melting point and good lubricity. Recommended for most engineering sectors, different components and machine elements, such as high-grade electrical and insulation material. Used to print semi-flexible thin parts and has a lower melting temperature than PA6 and PA66. Ultrafuse® PA can be printed at a lower temperature.
Ultrafuse® PA
Product Type
  • 3D Printing Polymers/ Photopolymers
  • PA (Polyamide, Nylon) > PA 6 (Nylon 6), other Copolymer
Physical Form
Product Status
Applications/ Recommended for
  • Engineering / manufacturing
  • Electrical markets
  • 3D Printing/Additive Manufacturing > Fuse deposition modeling
Key Features
  • Fatigue Resistant
  • Impact Resistance, Good
  • Strength, High
  • Viscosity, Medium
  • Wear resistance, Good

Ultrafuse® PA Properties

Thermal Properties

Value & Unit
Test Condition
Test Method
Deflection Temperature at 0.46 MPa (66 psi)
135 °C
( )

Ultrafuse® PA Processing Guidelines

3D Printing Properties

Value & Unit
Test Condition
Test Method
Nozzle Temperature
220 - 250 °C
Bed Temperature
90 - 120 °C
Nozzle Diameter
> 0.4 mm
Want to list or
update your products?
Want to report errors or
suggest improvements?
Access Reliable
Product Information

Database of 97205 Plastics & Elastomers,
reviewed and updated daily

Improve your Product
Selection Experience

Open your choices, compare products,
ask for samples, contact suppliers

Keep-up with latest
Technical Solutions

Be inspired and never miss again crucial
innovations with our weekly email updates

Back to Top